Titanium Gr 9 Bars

Name: Titanium Gr 9 Bars
Brand: Skyland Metal & Alloys Inc.
Price: 500.0 INR
Availability: InStock

Price 500.0 INR/ Piece

Get a Price/Quote

MOQ : 1 Kilograms

Titanium Gr 9 Bars Specification

Tensile Strength
620 MPa minimum

Thickness
Custom, generally 2mm to 100mm

Hardness
Rockwell C 20-32 (depends on hardness condition)

Thermal Conductivity
6.7 W/mK at 20C

Product Type
Bars / Rods

Types of Alloy
Titanium Alloys

Material
Titanium

Shape
Bar

Strength
High strength-to-weight ratio

Resistance
Excellent corrosion and oxidation resistance

Grade
GR 5

Melting Point
Approximately 1649C (3000F)

Density
4.48 Gram per cubic centimeter(g/cm3)

Chemical Composition
Ti-3Al-2.5V (Titanium 90%, Aluminum 3%, Vanadium 2.5%)

Color
Silver/Grey

Surface Finish
Smooth, bright, or as specified

Modulus of Elasticity
100 GPa

Application
Aerospace, marine, sports equipment, chemical processing

Yield Strength
483 MPa minimum

Compatibility
Biocompatible, suitable for medical applications

Size Range
Diameter: 6mm to 100mm, Length: up to 6000mm

Elongation
Minimum 10% in 50mm

Formability
Good cold forming properties

Standards
ASTM B348, ASME SB348, AMS 4921

Workability
Excellent weldability and machinability

Fatigue Strength
Superior fatigue resistance

Magnetism
Non-magnetic

Oxidation Resistance
Excellent up to 600C

Titanium Gr 9 Bars Trade Information

Minimum Order Quantity
1 Kilograms

Delivery Time
7 Days

About Titanium Gr 9 Bars

Titanium Grade 9 (Ti-9Al-2.5V) is a high-strength lightweight titanium alloy containing 9% aluminum and 2.5% vanadium, which gives it the right balance of strength and corrosion resistance. Its ability to perform well in extreme conditions, as well as its strength and durability in hard-wearing and corrosion-prone areas, makes it suitable for most industries

Superior Mechanical Properties

Titanium Grade 9 bars offer an optimal combination of high tensile strength (minimum 620 MPa), yield strength (minimum 483 MPa), and ductility (minimum 10% elongation in 50mm). With excellent fatigue resistance, they are particularly suitable for critical components subjected to cyclic loading in aerospace and marine applications.

Excellent Resistance and Durability

These titanium bars provide remarkable resistance to corrosion and oxidation, maintaining integrity even at elevated temperatures up to 600C. Their longevity is further assured by biocompatibility and non-magnetic properties, making them suitable for medical implants and chemical processing environments.

Versatile Applications and Customization

With a diameter range of 6mm to 100mm and lengths up to 6000mm, Titanium Grade 9 bars cater to various industry requirements. The availability of smooth or bright finishing options and customizable thicknesses enhance their usability across aerospace, marine, sports equipment, and medical sectors.

FAQ's of Titanium Gr 9 Bars:

Q: How are Titanium Grade 9 bars typically used in industry?

A: Titanium Grade 9 bars are primarily used in aerospace, marine, chemical processing, sports equipment, and medical industries. Their high strength-to-weight ratio and excellent corrosion resistance make them ideal for aircraft components, ship hardware, chemical plant equipment, bicycle frames, implants, and surgical devices.

Q: What standards do Titanium Grade 9 bars meet?

A: These bars are manufactured in accordance with ASTM B348, ASME SB348, and AMS 4921 standards, ensuring consistent quality and performance. Compliance with these standards makes them suitable for use in critical and regulated environments, such as aerospace and medical sectors.

Q: When should Titanium Grade 9 be preferred over other titanium grades?

A: Grade 9 is preferred when a balance of high strength, superior weldability, and formability is crucial. It is especially advantageous in situations where weight savings, fatigue strength, and resistance to harsh environments are primary requirements.

Q: Where can custom sizes or finishes for Titanium Grade 9 bars be obtained?

A: Custom sizes and surface finishes can be arranged through reputable exporters, importers, manufacturers, suppliers, or traders specializing in titanium products. Bars can be tailored within a diameter range of 6mm-100mm, thickness of 2mm-100mm, and lengths reaching up to 6000mm.

Q: What is the typical process for manufacturing Titanium Grade 9 bars?

A: The manufacturing process involves melting and alloying titanium with aluminum and vanadium, followed by hot or cold forming, precision machining, and heat treatment. The final bars are finished to customer specifications, ensuring required mechanical properties and surface finish are achieved.

Q: How does biocompatibility benefit the usage of Titanium Grade 9 bars?

A: Biocompatibility ensures that Titanium Grade 9 bars are safe for direct contact with biological tissues, making them well-suited for medical implants, surgical instruments, and other healthcare applications where material-tissue compatibility is crucial.

Tell us about your requirement