Titanium Gr 1 Tubing

Get a Price/Quote

MOQ : 10 Pieces

Titanium Gr 1 Tubing Specification

Tensile Strength
Minimum 240 MPa

Hardness
80 HB (Brinell Hardness)

Thickness
Custom/Tailored (typically 0.5mm to 5mm or as required)

Thermal Conductivity
16.3 W/mK

Product Type
tubing

Types of Alloy
Titanium Alloys

Material
Titanium

Shape
Pipe

Strength
Low to Moderate Strength

Resistance
Excellent Corrosion Resistance, Especially to Oxidizing and Reducing Environments

Grade
gr 1

Melting Point
1660C (3020F)

Density
4.51 Gram per cubic centimeter(g/cm3)

Chemical Composition
Titanium (Ti) 99.5%, Oxygen (O) 0.18%, Nitrogen (N) 0.03%, Carbon (C) 0.08%, Hydrogen (H) 0.015%, Iron (Fe) 0.20%

Color
Silver-Gray

Fabrication
Easily Formable, Good Machinability

Yield Strength
138 MPa (min)

Magnetic Properties
Non-Magnetic

Elongation
24% (min)

Form
Seamless and Welded

Density at 20C
4.51 x 103 kg/m3

Surface Condition
Smooth, Free from Scale and Crack

Standard Specification
ASTM B338 / ASTM B861

Outer Diameter Range
6.35 mm to 114.3 mm (custom on request)

Length
Up to 6000 mm (custom lengths available)

Modulus of Elasticity
105 GPa

Finish
Polished, Pickled, Annealed, or As Required

Applications
Heat Exchangers, Chemical Processing, Desalination Plants, Aerospace, Marine

Poisson's Ratio
0.34

Weldability
Excellent

Titanium Gr 1 Tubing Trade Information

Minimum Order Quantity
10 Pieces

Delivery Time
7 Days

About Titanium Gr 1 Tubing

Titanium gr 1 tubing is a popular material in the manufacturing industry due to its durability and lightweight properties. At the centre of these properties is the element titanium itself. Atomically, titanium consists of 22 protons, 22 electrons, and 24 neutrons. It has three principal isotopes (Ti-46, Ti-47, and Ti-48) and is a transition metal element that resides in group 4 of the periodic table. Here, its atomic number can be determined to be 22. Its typical form for titanium grade 1 tubing will have specific percentages of other metals, including oxygen and iron, to provide the durability and strength required for structural uses. In this alloy form, the material is corrosion-resistant and provides a strong structure in hostile working conditions.

Superior Corrosion Resistance

Titanium Gr 1 tubing stands out due to its exceptional resistance to corrosion, making it an ideal choice for environments exposed to aggressive chemicals or seawater. This inherent durability ensures prolonged service life in heat exchangers, desalination plants, and chemical processing units, offering reliable performance where it matters most.

Versatile Specifications and Customization

Meeting ASTM B338 and ASTM B861 standards, Titanium Gr 1 tubes are available in a wide range of diameters and lengths, with customization options to fulfill specific project needs. Both seamless and welded forms ensure flexibility for diverse industrial applications, addressing unique engineering requirements efficiently.

Easy Fabrication and Assembly

The machinability and formability of Titanium Gr 1 facilitate straightforward fabrication, allowing for easy bending, welding, and integration into assemblies. Its excellent weldability and smooth, scale-free surface make it advantageous across manufacturing and installation phases, minimizing complication and maximizing productivity.

FAQ's of Titanium Gr 1 Tubing:

Q: How can Titanium Gr 1 tubing be fabricated and welded?

A: Titanium Gr 1 tubing is known for its excellent weldability and ease of fabrication. It can be bent, formed, machined, or welded using conventional titanium techniques. Its smooth, pickled, or polished surface further simplifies welding and assembly, reducing the risk of contamination during the process.

Q: What applications benefit most from using Titanium Gr 1 tubing?

A: This tubing is particularly beneficial in heat exchangers, chemical processing plants, desalination units, marine engineering, and aerospace components due to its high corrosion resistance, formability, and lightweight nature. Its non-magnetic properties and smooth finish are also advantageous in these demanding applications.

Q: Where are custom sizes and finishes of Titanium Gr 1 tubing available?

A: Titanium Gr 1 tubing can be supplied in custom outer diameters (6.35 mm to 114.3 mm), lengths (up to 6000 mm), wall thicknesses, and finishes (polished, pickled, annealed, or as required) directly from leading exporters, manufacturers, suppliers, and traders. Specific requirements can typically be addressed upon request.

Q: What are the primary benefits of using Titanium Gr 1 tubing?

A: The main benefits include exceptional resistance to oxidizing and reducing environments, high ductility, low to moderate strength, excellent weldability, and a lightweight profile. Its long service life reduces maintenance costs and risk of failure in demanding chemical or marine environments.

Q: When should seamless versus welded Titanium Gr 1 tubing be chosen?

A: Seamless tubing is often preferred for high-stress, critical applications due to its superior uniformity and strength. Welded tubing is suitable for less critical uses where cost efficiency and custom lengths are priorities, without significant compromise on corrosion resistance or overall performance.

Q: How is the surface condition of Titanium Gr 1 tubing controlled during manufacturing?

A: The manufacturing process ensures a smooth surface finish, free from scale and crack formation. Options like polished, pickled, or annealed finishes are available to meet the requirements of different applications, ensuring optimal performance and aesthetics.