Monel K500 Stud Bolts

Name: Monel K500 Stud Bolts
Brand: Skyland Metal & Alloys Inc.
Price: 100.0 INR
Availability: InStock

Price 100.0 INR/ Kilograms

Get a Price/Quote

MOQ : 1 Kilograms

Monel K500 Stud Bolts Specification

Strength
Ultimate Tensile Strength: 965 MPa min

Standard
ASTM B865 / ASME SB865

Surface
Bright, Clean, Passivated

Temper
Annealed / Age Hardened

Purity
High Nickel-Copper Alloy

Hardness
Rockwell B88 - C34 (Annealed to Age Hardened)

Grade
Monel K500

Width
Diameter: 3 mm to 100 mm or as specified Meter (m)

Thickness
Available as per request (Custom) Meter

Material
Monel K500

Alloy
Nickel-Copper Alloy (Precipitation Hardened)

Shape
Other

Moisture
Corrosion Resistant (Non-Hygroscopic)

Chemical Composition
Ni 63%, Cu 27-33%, Al 2.3-3.15%, Ti 0.35-0.85%, Fe 2.0% max, Mn 1.5% max, Si 0.5% max, C 0.25% max, S 0.01% max

Application
Other

Dimension (L*W*H)
Standard and Custom sizes available Meter (m)

Color
Silvery Metallic

Connection Type
Threaded Both Ends

Corrosion Resistance
Excellent, especially Against Seawater and Industrial Acids

Elongation
20% min (in 50mm)

Tolerance
h6 / h7 or as specified

Melting Point
1315C (Approx.)

Yield Strength
690 MPa min

Heat Treatment
Solution Annealed, Precipitation Hardened

Finish
Plain, Passivated, as per Client Requirement

Length
Custom Lengths as per Drawing or Standard (Typically 10mm to 2000mm)

Service Temperature
Up to 600C

Weldability
Good (with suitable filler metals)

Magnetism
Non-Magnetic

Packing
Carton, Wooden Box, or As required by Client

Thread Type
Metric, UNC, UNF, BSW, Custom

Density
8.44 g/cm3

Monel K500 Stud Bolts Trade Information

Minimum Order Quantity
1 Kilograms

Delivery Time
7 Days

Monel K500 Stud Bolts About

Monel K500 stud bolts are produced from UNS N05500, a precipitation-hardenable nickel-copper alloy. Aluminium and titanium additions allow age hardening, giving K500 more than twice the strength of Monel 400 while retaining similar corrosion resistance. The alloy is non-magnetic down to -101C and performs well in seawater, hydrofluoric acid, and reducing acid environments. These stud bolts are used in offshore oil and gas, marine engineering, chemical processing, and subsea equipment where high strength, seawater resistance, and low magnetic permeability are all required together.